Scintillation and optical properties of Ce3+-doped CaGdAl3O7 single crystals
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Scintillation and optical properties of Ce3+-doped CaGdAl3O7 single crystals Scintillation and optical properties of Ce3+-doped CaGdAl3O7 single crystals](/preview/png/5397830.png)
چکیده انگلیسی
The single crystals of 0, 0.6, 1, 1.6 and 2 mol% Ce doped CaGdAl3O7 (Ce:CGAM) were grown by the Floating Zone method, and investigated on photoluminescence (PL) and scintillation properties. In the PL spectra, a broad emission appeared over 380-500 nm under 280 and 360 nm excitations with the quantum yield of 33.8-38.8%. Under a vacuum ultraviolet excitation (90 nm) using a synchrotron source, non-doped CGAM single crystal showed broad emissions over 250-650 nm. The PL decay time profiles followed a monotonic exponential decay with a decay time constant of around 33 ns. The scintillation spectra were similar to those of PL. All of the samples exhibited a clear photoabsorption peak and Compton edge in the pulse height spectra measured under 137Cs γ-ray irradiation, and the absolute scintillation light yield (LY) was highest for the 2% Ce-doped sample with the value of 3300±300 ph/MeV. The scintillation decay profiles were approximated by a third order exponential decay function, and the extracted decay time of Ce3+ emission component was around 36-44 ns. Among all the samples, 2%Ce:CGAM single crystal sample showed the best afterglow level as a scintillator under X-ray irradiation.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Luminescence - Volume 186, June 2017, Pages 93-97
Journal: Journal of Luminescence - Volume 186, June 2017, Pages 93-97
نویسندگان
Masaki Mori, Daisuke Nakauchi, Go Okada, Yutaka Fujimoto, Noriaki Kawaguchi, Masanori Koshimizu, Takayuki Yanagida,