Thermoluminescence study of Mn doped lithium tetraborate powder and pellet samples synthesized by solution combustion synthesis

In this paper, the thermoluminescence (TL) dosimetric characteristics under beta-ray, x-ray and gamma-ray excitations of powder and pellet Mn-doped lithium tetraborates (LTB) which were produced by solution combustion synthesis technique were investigated, and the results were compared with that of TLD-100 chips. The chemical composition and morphologies of the obtained LTB and Mn-doped LTB (LTB:Mn) were confirmed by X-ray diffraction (XRD), Fourier Transform Infrared (FTIR) and scanning electron microscopy (SEM) with EDX. LTB:Mn was studied using luminescence spectroscopy. In addition, the effects of sintering and annealing temperatures and times on the thermoluminescence (TL) properties of LTB:Mn were investigated. The glow curves of powder samples as well as pellet samples exposed to different beta doses exhibited a low temperature peak at about 100 °C followed by an intense principal high temperature peak at about 260 °C. The kinetic parameters (E, b, s) associated with the prominent glow peaks were estimated using Tm-Tstop, initial rise (IR) and computerized glow curve deconvolution (CGCD) methods. The TL response of integral TL output increased linearly with increasing the dose in the range of 0.1-10 Gy and was followed by a superlinearity up to 100 Gy both for powder and pellet samples using beta-rays. Powder and pellet LTB:Mn were irradiated to a known dose by a linear accelerator with 6 and 18 MV photon beams, 6-15 MeV electron beams and a traceable 137Cs beam to investigate energy response. Further, TL sensitivity, fading properties and recycling effects related with beta exposure of LTB:Mn phosphor were evaluated and its relative energy response was also compared with that of TLD-100 chips. The comparison of the results showed that the obtained phosphors have good TL dose response with adequate sensitivity and linearity for the measurement of medical doses.