Characterization of direct patterned Ag circuits for RF application
موضوعات مرتبط
مهندسی و علوم پایه مهندسی کامپیوتر سخت افزارها و معماری
پیش نمایش صفحه اول مقاله
Characterization of direct patterned Ag circuits for RF application
چکیده انگلیسی

We investigated the effects of sintering temperature on microstructural evolution and electrical characteristics of screen printed Ag patterns. A commercial conducting paste containing Ag nanoparticles was screen printed onto a Si substrate passivated with SiO2 and sintered under a sintering temperature range from 150 °C to 300 °C. Four point probe method was used to measure the DC resistance, while a network analyzer and Cascade’s probe system in the frequency range from 10 MHz to 30 GHz were employed to measure the S-parameters of the sintered Ag conducting patterns. The resistivity under the application of a DC decreased from 398 μΩ cm to 9 μΩ cm with increasing sintering temperature from 150 °C to 300 °C. From the measured S-parameters, the electrical losses in high frequencies also decreased with increasing sintering temperature (about 1.2 dB at 30 GHz) due to the formation of an interparticle neck after heat treatment at high temperatures.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Microelectronic Engineering - Volume 87, Issue 3, March 2010, Pages 379–382
نویسندگان
, , , , , , ,