عنوان انگلیسی مقاله ISI
Photoluminescence properties of U in SrBPO5 host: Effect of concentration and annealing temperature
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Photoluminescence properties of U in SrBPO5 host: Effect of concentration and annealing temperature Photoluminescence properties of U in SrBPO5 host: Effect of concentration and annealing temperature](/preview/png/5398774.png)
چکیده انگلیسی
Strontium borophosphate (SrBPO5) with and without uranium doped samples were synthesized through solid state reaction route in air atmosphere at different annealing temperatures. The dopant ion concentration was varied between 1 and 8 mol%. X-ray diffraction studies confirmed the formation of single phase compound in all the samples without any impurity phase up to 8 mol% of the dopant ion. The overall morphology and particle size was confirmed by scanning electron microscopic studies which suggested the presence of uneven, agglomerated particles with less than 1 µm individual size. It was observed that upon annealing at higher temperatures, the particles get agglomerated more and more with smooth boundaries. Photoluminescence (PL) studies confirmed stabilization of uranium as uranyl ion (UO22+) in the system. Based on the PL emission data concentration quenching was observed beyond 7 mol% of the dopant ion concentration. The critical distance (Lc) was estimated to be 3 Ã
suggesting Dexter type of energy transfer mechanism responsible for the quenching. The life time decay studies indicated the presence of two different types of environment around Uranyl ion. On annealing at temperatures beyond 900 °C the PL emission and decay time reduced drastically. It was concluded that on annealing at temperatures beyond 900 °C, defect centres get agglomerated around the metal ion providing non radiative pathways for the energy to get dissipated thereby reducing the PL emission and decay time. Color coordinates were evaluated for the 7 mol% uranium doped sample annealed at 900 °C. The values suggested that the system can be used as a potential green emitting phosphor material.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Luminescence - Volume 167, November 2015, Pages 45-50
Journal: Journal of Luminescence - Volume 167, November 2015, Pages 45-50
نویسندگان
Annapurna Rout, M. Mohapatra, N. Suriyamurthy, B.S. Panigrahi,