Facile combustion synthesized orthorhombic GdAlO3:Eu3+ nanophosphors: Structural and photoluminescence properties for WLEDs
چکیده انگلیسی
Nanoparticles of Eu3+ doped (1-11 mol%) GdAlO3 were prepared using low temperature (350 °C) solution combustion technique with gadalonium nitrate as oxidizer and oxalyl di-hydrazide (ODH) as a fuel. The synthesized samples were calcined at 1000 °C for 3 h and used for Powder X-ray diffraction (PXRD), Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy (SEM) and UV-visible absorption (UV-vis) characterization techniques. A pure orthorhombic was obtained in calcined samples. The average crystallite sizes were estimated using Scherrer's formula, W-H and size-strain plots and found to be in the range 25-50 nm and the same was confirmed by Transmission electron microscopy (TEM) studies. The phosphors exhibit bright red emission upon 395 nm excitation. The characteristic emission peaks recorded at ~591, 612, 654 and 694 nm (5D0→7Fj=1,2,3,4) were attributed to the 4f-4f intra-shell transitions of Eu3+ ions. The CIE chromaticity co-ordinates were calculated from emission spectra, the values (x, y) were very close to NTSC standard value of red emission. Further, the average CCT value was found to be ~2369 K, as a result the prepared nanophosphor was highly useful for red component of white light emitting devices and also for solid state display applications.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Luminescence - Volume 163, July 2015, Pages 47-54
نویسندگان
, , , , , , , , ,