Epitaxial growth and optical characterization of compound semiconductor β-FeSi2 prepared by pulsed laser deposition

β-FeSi2 thin films were prepared on FZ n-Si (1 1 1) substrates by pulsed laser deposition (PLD). The structural properties and crystallographic orientation of the films were investigated by X-ray diffraction (XRD) analysis. This indicates that β-FeSi2/Si (2 0 2/2 2 0) and the single-crystalline β-FeSi2 can be prepared using PLD. In photoluminescence (PL) measurements at 8 K detected by Ge detector, the PL spectra of the samples annealed at 900 °C for 1, 5, 8 and 20 h showed that the PL intensity of the A-band peak increased depending on annealing time in comparison with those of as-deposited samples. The intrinsic PL intensity of the A-band peak at 0.808 eV of the β-FeSi2 from the 20-h-annealed sample was investigated for the first time by the PLD method detected by an InGaAs detector. This result has been confirmed by temperature dependence and excitation power density of the 20-h-annealed sample with the comparison of other defect-related band peaks of the sample. Cross-sectional scanning electron microscopy (SEM) observation was also performed and the thickness of the thin films was found to be at 75 nm for 20-h-annealed. The thermal diffusion for the epitaxial growth of β−FeSi2/Si was observed when the compositional ratio of Fe to Si was around Fe:Si=1:2 for 20-h-annealed carried out by energy dispersive X-ray spectroscopy (EDX). We discussed high crystal quality of the epitaxial growth and optical characterization of β-FeSi2 achieved after annealing at 900 °C for 20 h.