Fluorescence enhancement of oxide fluoride glass co-doped with TbF3 and SmF3
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The fluorescence property of xTbF3-BaF2-AlF3-GeO2+ySmF3 (x=0.01-40Â mol%, y=0-5Â wt%) glasses were investigated. The enhancement of Sm3+ fluorescence was recognized in the presence of Tb3+. Increasing Tb3+ content, the emission color changed from green to orange. When the intensity of fluorescence at 540Â nm originated from Tb3+ is compared with that at 600Â nm originated from Sm3+, the information about the concentration quenching of Tb3+ and Sm3+ was obtained. From these results, rare earth ions were dispersed identically in the glasses. After heating to 673Â K or cooling to 77Â K, the emission color of 20TbF3-20BaF2-10AlF3-50GeO2/mol%+0.05Â wt% SmF3 glass was reversibly changed from orange to green. In addition, while the emission from 10TbF3-20BaF2-10AlF3-60GeO2+0.01Â wt% SmF3 glass was green, its crystallized sample, prepared by annealing at 1073Â K, exhibited an orange emission due to Sm3+ at room temperature.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Luminescence - Volume 126, Issue 2, October 2007, Pages 365-370
Journal: Journal of Luminescence - Volume 126, Issue 2, October 2007, Pages 365-370
نویسندگان
S. Nishibu, T. Nishio, S. Yonezawa, M. Takashima,