Investigation of RF sputtered PSG films for MEMS and semiconductor devices

In this work, we report the preparation of phospho-silicate-glass (PSG) films using RF magnetron sputtering process and its application as a sacrificial layer in surface micromachining technology. For this purpose, a 76 mm diameter target of phosphorus-doped silicon dioxide was prepared by conventional solid-state reaction route using P2O5 and SiO2 powders. The PSG films were deposited in a RF (13.56 MHz) magnetron sputtering system at 200–300 W RF power, 10–20 mTorr pressure and 45 mm target-to-substrate spacing without external substrate heating. To confirm the presence of phosphorus in the deposited films, hot-probe test and sheet resistance measurements were performed on silicon wafers following deposition of PSG film and a drive-in step. As a final confirmatory test, a p–n diode was fabricated in a p-type Si wafer using the deposited film as a source of phosphorus diffusion. The phosphorus concentration in the target and the deposited film were analyzed using energy dispersive X-rays (EDAX) tool. The etch rate of the PSG film in buffered HF was measured to be about 30 times higher as compared to that of thermally grown SiO2 films. The application of RF sputtered PSG film as sacrificial layer in surface micromachining technology has been explored. To demonstrate the compatibility with MEMS process, micro-cantilevers and micro-bridges of silicon nitride were fabricated using RF sputtered PSG as a sacrificial layer in surface micromachining. It is envisaged that the lower deposition temperature in RF sputtering (<150 °C) compared to CVD process for PSG film preparation is advantageous, particularly for making MEMS on temperature sensitive substrates.