Microstructural evolution of the as-cast and the peak-aged Mg-xYb-0.5Zn-0.4Zr (x = 0.5, 1, 2, and 3 wt.%) alloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Microstructural evolution of the as-cast and the peak-aged Mg-xYb-0.5Zn-0.4Zr (x = 0.5, 1, 2, and 3 wt.%) alloy Microstructural evolution of the as-cast and the peak-aged Mg-xYb-0.5Zn-0.4Zr (x = 0.5, 1, 2, and 3 wt.%) alloy](/preview/png/5459350.png)
چکیده انگلیسی
Detailed microstructures of the as-cast and the peak-aged metal mould casting Mg-xYb-0.5Zn-0.4Zr (x = 0.5, 1, 2, and 3 wt.%) alloys were thoroughly investigated. The results indicate that Yb has better grain refinement effect on the Mg-Zn-Zr based alloys compared with the conventional rare earth elements such as Nd, Sm, and Gd, and the dominant intermetallic phase in the as-cast samples is Mg2Yb, although with a few Mg41Sm5 particles. In addition, the studied alloys also exhibit good aging hardening response when aged at 200 °C. During aging treatment, obvious precipitation of T phase formed on grain boundaries can be observed in the alloys with Yb is less than 2 wt.%, while Mg2Yb precipitate chains in the grain center and discrete Mg2Yb particles homogeneously distributed near grain boundaries in the samples with Yb addition over 2 wt.%. Finally, ultra-fine needle-like precipitates were detected in all peak-aged samples, although with distinct difference on sizes and distribution densities. Based on energy dispersive spectrometer mappings of Mg, Yb, Zn and Zr and the SAED patterns, the needle-like precipitates were identified as γⲠphase (MgZnRE containing, hexagonal structure, a = 0.55 nm and c = 0.52 nm) and followed an orientation relationship as (11¯.0)γâ²||(11.0)Mg and [00.1]γâ²||[00.1]Mg.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 726, 5 December 2017, Pages 295-305
Journal: Journal of Alloys and Compounds - Volume 726, 5 December 2017, Pages 295-305
نویسندگان
Deping Zhang, Qiang Yang, Dongdong Zhang, Qi Sui, Xin Qiu, Hui Li, Kai Guan, Hong Zhou, Jian Meng,