Magnetostructural phase transitions and magnetocaloric effects in as-cast Mn1-xAlxCoGe compounds
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
The structural and magnetic properties of as-cast Mn1-xAlxCoGe (0 â¤Â x â¤Â 0.05) have been studied by X-ray diffraction, differential scanning calorimetry, and magnetization measurements. The partial substitution of Al for Mn in Mn1-xAlxCoGe results in a decrease in the martensitic transition temperature TM. For the concentration range 0 â¤Â x â¤Â 0.01, TM was found to coincide with ferromagnetic transition temperature (TC) resulting in a first-order magnetostructural transition (MST). A further increase in aluminum concentration resulted in a splitting of the phase transition temperatures, which included a drastic decrease in the martensitic temperature. The compounds with x > 0.02 showed a single transition at TC. The maximum values of the magnetic entropy changes (-ÎSM) were â¼18 J/kgK, 12 J/kgK, and 7 J/kgK for ÎH = 5T at 313 K (x = 0.00), 286 K (x = 0.01), and 220 K (x = 0.02), respectively. The maximum value of the relative cooling power (RCP) was found to be 303 J/kg for x = 0.01 at T = 286 K for ÎH = 5T. It has been established that as-cast samples of this system show large value of MCE near room temperature making this system a promising material for magnetic cooling technologies.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 709, 30 June 2017, Pages 142-146
Journal: Journal of Alloys and Compounds - Volume 709, 30 June 2017, Pages 142-146
نویسندگان
Anil Aryal, Abdiel Quetz, Sudip Pandey, Tapas Samanta, Igor Dubenko, Margaret Hill, Dipanjan Mazumdar, Shane Stadler, Naushad Ali,