Insights into structure and function of high pressure-modified starches with different crystalline polymorphs
ترجمه فارسی عنوان
آماری از ساختار و عملکرد نشاسته اصلاح شده با فشار با پلی مورفهای مختلف بلوری
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
علوم زیستی و بیوفناوری
بیوشیمی، ژنتیک و زیست شناسی مولکولی
زیست شیمی
چکیده انگلیسی
The effect of high pressure (HP) treatment at 200-600Â MPa for 30Â min on properties of three starches with different polymorphs was investigated. HP treatment altered greatly the morphology of wheat starch, especially at 400Â MPa or higher. The crystallinity of wheat starch decreased from 22.6% for native starch to 3.4% for starch after treatment at 600Â MPa. The short-range molecular order as measured by FTIR and Raman spectroscopy decreased with increasing treatment pressure. HP treatment had little effect on structural properties of potato and yam starches, except for yam starch after treatment at 600Â MPa. HP treatment decreased the pasting viscosities of wheat starch except for the treatment at 200Â MPa, which increased the peak, trough and final viscosities by 6.7, 11.1 and 5.7%, respectively. The peak viscosity of potato and yam starches was increased respectively by 14.0 and 11.3% after HP treatment at 600Â MPa. HP treatment at 600Â MPa enhanced greatly the final digestion percentages of wheat and yam starch by 20 and 26.4%, but had little effect on potato starch. The above results showed that wheat starch was more susceptible to the effects of HP treatment than did yam and potato starches, and that C-type yam starch behaved more likely the B-type potato starch to HP treatment.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Biological Macromolecules - Volume 102, September 2017, Pages 414-424
Journal: International Journal of Biological Macromolecules - Volume 102, September 2017, Pages 414-424
نویسندگان
Jinrong Wang, Huaping Zhu, Sha Li, Shujun Wang, Shuo Wang, Les Copeland,