Triticale extrudates - Changes of macrostructure, mechanical properties and molecular water dynamics during hydration

As a result of storage at the highest hydration level (aw = 0.981) contraction of snacks was observed. The shrinkage was more pronounced in case of extrudates obtained from raw material containing 16% of water regardless of the extrusion temperature. The hardness of extrudates depended both on the feed moisture and hydration. Samples obtained from the raw material containing 20% moisture were harder than those prepared at the feed moisture of 16%. Based on the results of molecular dynamics study by low field NMR technique, a model of hydration was developed and critical hydration value of extruded snacks was calculated. Higher values of the critical hydration were obtained for snacks extruded at temperature 135 °C than for those obtained at 175 °C. The feed moisture level affected critical hydration values to a lesser extent. Obtained results suggest that the state of water in extrudates depends on extrusion process conditions.