![عکس صفحه اول مقاله: Direct stöber synthesis of monodisperse silica particles functionalized with mercapto-, vinyl- and aminopropylsilanes in alcohol–water mixed solvents Direct stöber synthesis of monodisperse silica particles functionalized with mercapto-, vinyl- and aminopropylsilanes in alcohol–water mixed solvents](/preview/png/593670.png)
In this study we explore the preparation of 3-mercaptopropyl-, vinyl- and 3-aminopropyl-functionalized silica monodisperse nanoparticles by direct synthesis (`one-pot synthesis') in alcohol–water mixed solvents. These functionalized monodisperse silicas are denoted as MP-silica, V-silica and AP-silica, respectively. Monodisperse particles with diameters ranging from several tens to one hundred nanometers were successfully prepared, and dispersion was confirmed by dynamic light scattering. The synthetic conditions that were required to achieve monodispersion differed considerably among the different types of organic functional groups. The change in particle size were mainly influenced by the concentration of ammonia, by the mixing ratio of organosilica against TEOS and by the solvent composition for MP-silica, V-silica and AP-silica, respectively. The shapes of the monodisperse nanoparticles were revealed as being spherical by SEM observations. The organic functional groups were analysed by IR and Raman vibrational spectroscopies. We show experimental evidence for the formation of SS bonds in MP-silica, and a considerable blue shift of the NH2 scissor vibration in AP-silica.
Figure optionsDownload as PowerPoint slideHighlights
► One pot Stöber synthesis was applied to the preparation of monodisperse functionalized silica nanoparticles.
► Type of alcohol in the mixed solvent depends on the functional groups.
► The particle size can be changed with the concentration of organosilane, alcohol and NH4+.
► Structural analysis was carried out by vibrational spectroscopies.