![عکس صفحه اول مقاله: Synthesis and characterization of belt-like VO2(B)@carbon and V2O3@carbon core–shell structured composites Synthesis and characterization of belt-like VO2(B)@carbon and V2O3@carbon core–shell structured composites](/preview/png/594298.png)
VO2(B) nanobelts encapsulated into carbon core–shell structured composite (VO2(B)@C) was successfully synthesized using VO2(B) nanobelts as the cores and glucose as the shells via an environmental hydrothermal method. The “adsorption carbonization growth” (ACG) mechanism was proposed to explain the formation of VO2(B)@C. The influence of synthetic parameters, such as, the reaction temperature, concentration of glucose and reaction time, was systematically investigated to control the fabrication of VO2(B)@C. Subsequently, belt-like V2O3@C core–shell structured composite was prepared by the heating treatment of VO2(B)@C. Furthermore, the electrochemical properties of this novel belt-like V2O3@C core–shell structured composite was studied, indicating that it exhibits an initial discharge capacity of as high as 162 mAh/g and the discharge capacity is still 104, 89, 67 mAh/g after 30, 50, and 89 cycles, which is much higher than pure V2O3. The phase transition properties of V2O3 powder and V2O3@C composite were investigated by DSC, which revealed that V2O3@C has the same phase transition properties of V2O3. The as-obtained V2O3@C composite has potential applications to the cathode and functional positive temperature coefficient (PTC) materials.
Figure optionsDownload as PowerPoint slideHighlights
► VO2(B)@C core–shell structured composite has been successfully synthesized.
► The ACG mechanism was proposed to explain the formation of VO2(B)@C.
► Belt-like V2O3@C composite was first prepared using VO2(B)@C as the precursor.
► The electrochemical property of V2O3 has been greatly improved by V2O3@C.
► V2O3@C core–shell composite owns the phase transition property of V2O3.
Journal: Colloids and Surfaces A: Physicochemical and Engineering Aspects - Volume 396, 20 February 2012, Pages 144–152