Drying processes for preparation of titania aerogel using supercritical carbon dioxide

Supercritical carbon dioxide drying was performed for the preparation of titania aerogels from sol–gel routes. The conditions of supercritical carbon dioxide drying were 313–323 K and 7.8–15.5 MPa. The solvents in titania wet gels obtained from the sol–gel routes were replaced by acetone. The titania aerogels obtained from supercritical carbon dioxide drying form needle-like structures. In supercritical carbon dioxide drying, the extraction rates of acetone from the wet gels were measured by using an on-line Fourier transform infrared spectroscope. It was found that the titania aerogels with lower cohesion were induced from the formations of homogenous phase for carbon dioxide + acetone system and the lower extraction rates of acetone. Furthermore, titania films were prepared by the depositions of the titania aerogels on ITO-coated PET substrates. The needle-like aerogels with lower cohesion derive the titania film with high surface area.