![عکس صفحه اول مقاله: A facile route to synthesis of S-doped TiO2 nanoparticles for photocatalytic activity A facile route to synthesis of S-doped TiO2 nanoparticles for photocatalytic activity](/preview/png/64957.png)
• Synthesis of TiO2 doped with S.
• Detailed characterisation of novel materials.
• Decomposition of malachite green from water.
There is always a market for cost effective methods of pollution degradation and one of the best areas to keep costs down is through synthesis techniques. This paper provides a simple technique to synthesise porous TiO2 nanoparticles with increased surface area through a scaffold template technique. Their photocatalytic activity is enhanced by incorporating sulphur as a dopant and were validated by analysing the degradation of malachite green (MG). The materials were doped at a molar ratio of 100:1 (Ti:S) and calcined at different temperatures to adjust the anatase/rutile content. Detailed characterisation of the materials was undertaken using XRD, BET, XPS, TEM and FTIR. The nanoparticles displayed a microporous structure and had an increased surface area of 115 m2 g−1 which was reduced by doping and temperature induced phase transformation. Photocatalytic testing showed that the doped materials calcined at 700 °C preformed the best in. It was observed that 20 mg l−1 of MG was decomposed in 30 min using a 40 W UV bulb at pH 9 and the results surpassed those achieved by the commercial catalyst P25 which was also tested for comparison.
Figure optionsDownload high-quality image (78 K)Download as PowerPoint slide
Journal: Journal of Molecular Catalysis A: Chemical - Volume 406, September 2015, Pages 51–57