The effects of Al doping and post-annealing via intrinsic defects on photoluminescence properties of ZnO:Eu nanosheets

Europium (Eu) and Aluminum (Al) co-doped ZnO nanosheets were synthesized by a hydrothermal method. The effects of Al concentration as a dopant and post-annealing of ZnO:Eu nanosheets on its structural, electrical and optical properties were investigated in detail. Prepared samples were characterized structurally using X-ray diffraction (XRD), morphologically using scanning electron microscopy (SEM) and optically using photoluminescence (PL) spectroscopy analyses. No diffraction peak related to dopants in XRD spectrum along with shift in peaks angles relevant to ZnO proved that Al and Eu ions were doped successfully into ZnO nanosheets. This study recommends that extrinsic doping and intrinsic defects have impressive roles on transferring energy to Eu ions at indirect excitations. Based on photoluminescence observations, intra-4f transitions of Eu3+ ions at an excitation wavelength of 390 nm allow a sharp red luminescence. Also the results showed that optical properties of ZnO can be tuned by varying the amount of Al concentration. In comparison with annealed Al doped ZnO:Eu nanostructures, as-grown samples showed the stronger PL peaks which indicated the effective role of intrinsic defects beside of extrinsic doping on energy transfer from ZnO host to Eu3+ ions which consequently led to producing the strong red emission from these sites.