Effect of processing parameter on structural, optical and electrical properties of photovoltaic chalcogenide nanostructured RF magnetron sputtered thin absorbing films

The aim of this work was to develop high quality of CuIn1−xGaxSe2 thin absorbing films with x (Ga/In+Ga)<0.3 by sputtering without selenization process. CuIn0.8Ga0.2Se2 (CIGS) thin absorbing films were deposited on soda lime glass substrate by RF magnetron sputtering using single quaternary chalcogenide (CIGS) target. The effect of substrate temperature, sputtering power & working pressure on structural, morphological, optical and electrical properties of deposited films were studied. CIGS thin films were characterised by X-ray diffraction (XRD), Field emission scanning electron microscope (FE-SEM), Energy dispersive X-ray spectroscopy (EDAX), Atomic force microscopy (AFM), UV–vis–NIR spectroscopy and four probe methods. It was observed that microstructure, surface morphology, elemental composition, transmittance as well as conductivity of thin films were strongly dependent on deposition parameters. The optimum parameters for CIGS thin films were obtained at a power 100 W, pressure 5 mT and substrate temperature 500 °C. XRD revealed that thin film deposited at above said parameters was polycrystalline in nature with larger crystallite size (32 nm) and low dislocation density (0.97×1015 lines m−2). The deposited film also showed preferred orientation along (112) plane. The morphology of the film depicted by FE-SEM was compact and uniform without any micro cracks and pits. The deposited film exhibited good stoichiometry (Ga/In+Ga=0.19 and In/In+Ga=0.8) with desired Cu/In+Ga ratio (0.92), which is essential for high efficiency solar cells. Transmittance of deposited film was found to be very low (1.09%). The absorption coefficient of film was ~105 cm−1 for high energy photon. The band gap of CIGS thin film evaluated from transmission data was found to be 1.13 eV which is optimum for solar cell application. The electrical conductivity (7.87 Ω−1 cm−1) of deposited CIGS thin film at optimum parameters was also high enough for practical purpose.