Structural and thermal stability of mesoporous alumina synthesized by Al-based coordination polymer

Mesoporous alumina with a narrow pore size distribution is synthesized by direct thermolysis of Al-based coordination polymer. By applying the appropriate thermolysis temperature, both high surface area and large pore volume are obtained with the collapses and elimination of the 1,4-benzenedicarboxylate linkers of Al-based coordination polymer. This new class of mesoporous alumina display better adsorption properties and higher thermal stability, which retain mesoporous properties and high surface area after calcination in 900 °C. This thermolysis method provides a new approach to synthesize mesoporous alumina with high thermal stability by using coordination polymers.

The nanostructured mesoporous alumina was synthesized via a thermal process by using MIL-53(Al). The structure of MIL-53(Al) consists of a three-dimensional framework built up from the interconnection of infinite chains of corner-sharing octahedral AlO4(OH)2 with 1,4-benzenedicarboxylate ligands. After heating above 530 °C, the benzenedicarboxylate (BDC) linker gradually collapses from framework and MIL-53(Al) is transformed into amorphous Al2O3 at 650 °C for 10 h. During the process of elimination of BDC linker, the octahedral AlO4(OH)2 maintain the layer alignment of their parent MIL-53(Al) and amorphous alumina channels with highly arrangements can be obtained.Figure optionsDownload as PowerPoint slideHighlights
► Crystalline mesoporous alumina is synthesized by direct thermolysis of Al-based coordination polymer.
► Obtained mesoporous alumina display better adsorption properties and higher thermal stability.
► This thermolysis method provides a new approach to synthesize crystalline mesoporous alumina.