Sensitization induced stress corrosion failure of AISI 347 stainless steel fractionator furnace tubes

Austenitic stainless steel tubes are used as furnace tubes in petrochemical industries mainly because of their corrosion resistance and mechanical strength. AISI 347 grade stainless steel is used as furnace heater tubes in the fractionator of hydrocracker unit. Even though this stainless steel is stabilized with the addition of niobium thus preventing sensitization related corrosion failures, operational and maintenance errors may result in premature failures if conditions prevail. The present work reports the premature failure of AISI 347 grade fractionator furnace tubes after nearly 8 years of service. The failure occurred after shutdown. Carbonaceous deposits were found on the inner walls of the tube and circumferential cracks were found beneath the deposit. The service exposed 347 SS alloy tube was in the sensitized condition as confirmed by microstructure and double loop electrochemical potentiodynamic reactivation test. The tube material got sensitized possibly by localized overheating at the carbon layer deposited site. During shutdown of hydrocracker unit polythionic acid formation occurred possibly due to errors in shutdown procedures. Sensitized alloy 347 tube undergone polythionic acid induced intergranular stress corrosion cracking (PASCC).

► AISI 347 SS tube failure of hydrocracker furnace was investigated.
► Microstructure and DL-EPR tests showed sensitization of service exposed AISI 347 SS.
► Coke deposition on tube inner wall caused localized heating and then sensitization.
► Polythionic acid formation at shutdown period caused SCC of sensitized tube.