Manufacturing defects and the evidence of thermomechanical fatigue in a ceramic vacuum furnace tube
چکیده انگلیسی

Efforts were directed towards a post-mortem failure analysis of a silicon-carbide tube that failed after cyclic operation in a vacuum furnace. In formulating a plausible scenario for the failure of the reaction-bonded tube, both the fracture record retained by the tube remnants and service history were analyzed. Results of the fractographic analysis indicated thermomechanically induced low-cycle fatigue in the silicon-carbide originating from severe defects on the internal (heated) surface. These defects were the result of poor infiltration of silicon into resident porosity during the fabrication of the tube. A review of the service history confirmed the likelihood of a fatigue scenario because of potentially deleterious explosions caused by delayed burner ignition in addition to operational thermal-transients experienced during forced cool-downs.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Engineering Failure Analysis - Volume 13, Issue 7, October 2006, Pages 1184–1190
نویسندگان
,