High strain rate deformation and cracking of AA 2219 aluminium alloy welded propellant tank

Aluminium alloy AA 2219 (Al–6.6Cu–1Mn) is the candidate material for the fabrication of propellant storage tank of launch vehicle. Cold rolled sheets of 6.5 mm thickness are used to make the cylindrical shell, while sheets of 4.5 mm thickness are used for the construction of dome through petal forming technique. Petals, formed through cone rolling, treated to T87 temper condition are welded together by TIG welding to configure the dome. Such domes are joined to the cylindrical shell through a ring by TIG welding.The upper stage consists of two tanks, one oxidizer tank (liq. O2) and other fuel tank (liq. H2). After completing various developmental qualification tests, propellant flow rate test of one of the system was carried out. Almost all the liquid oxygen of the tank was removed and only a little quantity remained at the bottom. During one of the subsequent tests; when dry nitrogen gas was purged to evaporate the remaining liquid oxygen, the oxidizer tank dome catastrophically fractured with an audible sound. Fracture of oxidizer tank dome, placed at lower part of the system caused excessive deformation and subsequently it also caused fracture of fuel tank dome placed just over it.Detailed metallurgical investigations were carried out on the failed components and it was found that the tank failed under very high strain rate deformation. This paper brings out the details of the investigation carried out.