The root cause for cracking of rear brake components occurred during cold forming process was investigated. Optical micrographs showed the abundance of extended inclusions with several rounded ones in the steel. SEM image revealed the fracture surface which contained many extended cavities formed by extended inclusions and dimples all indicating a ductile rupture. EDS analysis confirmed that the extended inclusions were MnS type while the rounded ones were formed as a result of Ca-treatment. The crack propagation along with inclusions was clearly observed on the polished planes and on the fracture surface. It was determined that MnS type inclusions were the root cause for the cracking phenomena. The abundance of extended MnS inclusions indicated insufficient inclusion modification through Ca-treatment and insufficient removal of these inclusions in failed steel.
Journal: Engineering Failure Analysis - Volume 15, Issue 4, June 2008, Pages 295–301