Hydrogen permeation through dense BaCe0.8Y0.2O3âδ - Ce0.8Y0.2O2âδ composite-ceramic hydrogen separation membranes
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Hydrogen permeation through dense BaCe0.8Y0.2O3âδ - Ce0.8Y0.2O2âδ composite-ceramic hydrogen separation membranes Hydrogen permeation through dense BaCe0.8Y0.2O3âδ - Ce0.8Y0.2O2âδ composite-ceramic hydrogen separation membranes](/preview/png/7712018.png)
چکیده انگلیسی
This report quantifies hydrogen permeation through dense 50/50 wt.-% BaCe0.8Y0.2O3âδ - Ce0.8Y0.2O2âδ membranes in which BaCe0.8Y0.2O3âδ serves as a proton conductor and Ce0.8Y0.2O2âδ serves as an electron conductor. A maximum hydrogen flux of 0.0744 mL cmâ2 minâ1 (5.54 Ã 10â4 mol mâ2 sâ1) at 900° C is observed through a 1.44-mm-thick membrane with a 0.5 atm hydrogen partial pressure gradient. This results in a permeability of 0.0107 mL cmâ1 minâ1 when normalized by thickness. This is one of the highest permeabilities reported to date for proton-conducting ceramic membranes. While permeation rates through BaCe0.8Y0.2O3âδ - Ce0.8Y0.2O2âδ membranes are promising, membrane performance is found to degrade over time. The source of degradation is hypothesized to be the formation of a dopant-deficient phase on the feed-side membrane surface which creates an increased inter-granular contact resistance. Additionally, Ni metal particles are observed inside of internal pores, and at grain boundaries between BaCe0.8Y0.2O3âδ and Ce0.8Y0.2O2âδ grains, indicating the reduction of the NiO used in solid-state reactive sintering during device operation. These particles may contribute to increased mechanical stresses between grains and subsequent membrane fracture. While the permeation demonstrated by these composite membranes is encouraging, further development is needed before these novel materials can be used in commercial applications.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Hydrogen Energy - Volume 41, Issue 4, 30 January 2016, Pages 2598-2606
Journal: International Journal of Hydrogen Energy - Volume 41, Issue 4, 30 January 2016, Pages 2598-2606
نویسندگان
Wade A. Rosensteel, Sandrine Ricote, Neal P. Sullivan,