Chitosan microparticles based polyelectrolyte complex scaffolds for bone tissue engineering in vitro and effect of calcium phosphate

Chitosan microparticles were mixed with chitosan and carboxymethyl cellulose solution to achieve a good binding between the microparticles. Three different compositions of scaffolds were made by varying the calcium phosphate (CaP) amount: 0%, 10%, and 20%. Potassium chloride was used as salt, to make pores inside the scaffolds after leaching out when immersed in phosphate buffer saline (PBS). Compressive strength and compressive modulus of both non-porous (before leaching out), and porous (after leaching out) scaffolds were measured according to the ASTM standards. The highest compressive strength of 27 MPa was reported on 10% CaP scaffolds while 20% CaP scaffolds showed the lowest. The increasing CaP content reduces the compressive strength of the scaffolds. The highest wet state compressive strength was reported on 0% CaP scaffolds with 0.36 MPs and 0.40 MPa at day 1 and day 3 respectively. In vitro cell culture studies showed good cell adhesion and cell proliferation on 10% CaP scaffolds.