عنوان انگلیسی مقاله ISI
Fabrication and characterization of porous biphasic β-tricalcium phosphate/carbonate apatite alginate coated scaffolds
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
In this research, biphasic β-tricalcium phosphate/carbonate apatite (β-TCP/CO3Ap) scaffolds incorporated with alginate were fabricated. Sodium alginate was extracted from local brown seaweed, Sargassum polycystum via calcium alginate process. Biphasic β-TCP/CO3Ap scaffolds were fabricated by polymer reticulate method. β-TCP slurry was infiltrated into the polyurethane foam (PU) foam, then sintered up to 1300â¯Â°C, soaked for 4â¯h and immediately quenched in still air to form biphasic β-TCP/α-TCP scaffold. Biphasic β-TCP/α-TCP scaffold was then transformed to biphasic β-TCP/CO3Ap scaffold by dissolution-precipitation reaction with 1â¯M of NaHCO3 at 170â¯Â°C for 1, 3 and 5 days. Biphasic β-TCP/CO3Ap scaffold from 5 days dissolution-precipitation reaction was chosen to incorporate with 1%, 3% and 5% of sodium alginate, respectively, as it has the highest composition of CO3Ap phase. FTIR and FESEM analysis confirmed the presence of characteristic functional groups of sodium alginate. Mechanical strength of biphasic β-TCP/CO3Ap scaffold improved by increasing the concentration of sodium alginate. The highest mechanical strength achieved was 26.38 kPa for biphasic β-TCP/CO3Ap scaffold with 5% sodium alginate coating and it was chosen to further study with the addition of 1%, 3% and 5% microspheres. FESEM analysis confirmed the attachment of microspheres on the surface of alginate/biphasic β-TCP/CO3Ap scaffold was successful.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 44, Issue 8, 1 June 2018, Pages 9499-9505
Journal: Ceramics International - Volume 44, Issue 8, 1 June 2018, Pages 9499-9505
نویسندگان
Xuan Hui Yong, Muhammad Iqbal Mazlam, Nurazreena Ahmad,