عنوان انگلیسی مقاله ISI
Densification and microstructure of magnesium aluminate spinel for adding method of Sc2O3
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Densification and microstructure of magnesium aluminate spinel for adding method of Sc2O3 Densification and microstructure of magnesium aluminate spinel for adding method of Sc2O3](/preview/png/7994599.png)
چکیده انگلیسی
The effect of adding method of Sc2O3 on the densification and microstructure of magnesium aluminate spinel prepared by co-precipitated method was investigated. Sintered products were characterized in terms of densification, phase analysis, quantitative elemental analysis, microstructure and flexural strength. Sintering additives were added in the form of Sc salt and in the form of scandium oxide, respectively. No matter in what way to add, sintering additives exist in the form of Sc2O3. Moreover, incorporating of Sc3+ into the spinel structure increases lattice parameters, which improves the diffusion, mass transfer, and densification. The microstructure of sintered samples with adding Sc salt as a sintering additive is more compact and the grain size distribution is more uniform although their grain size is larger compared with that of sintered samples with adding scandium oxide as a sintering additive. Moreover, the optimum flexural strength (97 MPa) of the sintered products is obtained on sintering at 1650 °C with the addition of Sc salt.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 735, 25 February 2018, Pages 394-399
Journal: Journal of Alloys and Compounds - Volume 735, 25 February 2018, Pages 394-399
نویسندگان
Jianhua Liu, Xiaojun Lv, Jie Li, Libo Zhang, Jinhui Peng,