Mechanical and thermal physical properties, and thermal shock behavior of (ZrB2 + SiC) reinforced Zr3[Al(Si)]4C6 composite prepared by in situ hot-pressing
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
Mechanical and thermal physical properties, and thermal shock behavior of (ZrB2 + SiC) reinforced Zr3[Al(Si)]4C6 composite prepared by in situ hot-pressing
چکیده انگلیسی
The mechanical and thermal physical properties, as well as thermal shock behavior of in situ hot-pressed 30 vol.% (ZrB2 + SiC)/Zr3[Al(Si)]4C6 composite have been investigated and compared with monolithic Zr3[Al(Si)]4C6 ceramic. The composite shows superior hardness (Vickers hardness of 17.5 GPa), stiffness (Young's modulus of 418 GPa), strength (room-temperature bending strength of 648 MPa, and high-temperature bending strength of 439 MPa at 1300 °C in air), and toughness (fracture toughness of 7.69 MPa m1/2) compared with Zr3[Al(Si)]4C6. The composite can retain a high modulus of 362 GPa at 1350 °C (87% of that at ambient temperature). In addition, the composite exhibits higher specific heat capacity and thermal conductivity but slightly lower coefficient of thermal expansion compared with Zr3[Al(Si)]4C6. The critical thermal shock temperature difference (ΔTc) increases from 225 °C for Zr3[Al(Si)]4C6 to 345 °C for the composite, and the calculation results of thermal shock resistance parameters also indicate a much improved thermal shock resistance of the composite.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 619, 15 January 2015, Pages 338-344
نویسندگان
, , , , ,