Influence of formic acid on the microstructure and corrosion resistance of Zn-Ni alloy coatings by electrodeposition
ترجمه فارسی عنوان
تأثیر اسید فسفریک بر روی ریزساختار و مقاومت خوردگی پوشش های آلومینیوم روی آن به وسیله قرار دادن الکترواستاتیک
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
چکیده انگلیسی
In this study the effect on the deposition efficiency and corrosion resistance of Zn-Ni electrodeposits after the addition of formic acid (0.03 to 0.53Â mol/L) to the plating bath is investigated. The corrosion resistance was evaluated in an aerated solution of 2.0Â mol/L NaOH and 0.5Â mol/L NaCl using weight loss tests and electrochemical measurements, potentiodynamic polarization curves and electrochemical impedance spectroscopy measurements. The addition of formic acid to chemical bath enhanced the corrosion resistance of the Zn-Ni deposit in both solutions. Above 0.07Â mol/L formic acid added to the solution, which corresponds to pHÂ 3.0, the corrosion rate does not vary significantly. Improved corrosion resistance, by adding 0.07Â mol/L formic acid, was found in deposits obtained from chemical bath with the same pH. The addition of formic acid to the chemical bath of the Zn-Ni deposit produces an enhancement in the efficiency of galvanostatic deposition when the pH of the bath is maintained at approximately pHÂ 3.0. It was observed that the addition of formic acid changes the structure of the Zn-Ni deposit due to the presence of the Ni5Zn21 intermetallic phase.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Surface and Coatings Technology - Volume 258, 15 November 2014, Pages 232-239