Stability enhancement of P3HT:PCBM polymer solar cells using thermally evaporated MoO3 anode buffer layer

Polymer solar cells have been fabricated with thermally evaporated MoO3 as anode buffer layer (ABL). The stability of MoO3 and PEDOT:PSS based devices was examined under different test conditions. The MoO3 based device exhibited a slightly better efficiency and significantly higher stability compared to PEDOT:PSS based device. At a relative humidity of 45% the unencapsulated PEDOT:PSS based device degraded completely within 96 h. On the other hand, MoO3 based device retained more than 60% of its initial efficiency after 96 h. The reason behind stability enhancement was investigated by measuring time-evolution of reflectance and hole-current. Experimental results revealed that the stability enhancement for MoO3 based device originates from the reduction in degradation of anode/active layer interface.