Iron modified structural and optical spectral properties of bismuth silicate glasses

Iron bismuth silicate glasses have been successfully synthesized by melt quenching technique. The amorphous nature of the glass samples is ascertained by the XRD patterns. The values of density, molar volume and crystalline volume have been measured and are found to decrease with increase in iron content. The glass transition temperature measured using Differential Scanning Calorimetry (DSC) also varies with increase in Fe2O3 content. The Raman and FTIR spectra of the studied glass system taken at room temperature suggests that Fe2O3 modifies the structure of bismuth silicate glasses and it acts as both network modifier as well as network former. Bismuth also plays the role of both network modifier (BiO6 octahedra) as well as network former (BiO3 pyramids) and SiO2 exists in SiO4 tetrahedral structural units with two non-bridging oxygens. The Hydrogenic excitonic model is found to be applicable to the studied glass compositions. The variation in Urbach energy value observed for the studied glass samples suggests the possibility of increase in the number of glass defects. The metallization criterion for the synthesized glass samples is determined and found to be in the range 0.30-0.38.