Radiation-induced segregation at grain boundaries in AL-6XN stainless steels irradiated by hydrogen ions

The effect of high concentration of hydrogen on the segregation of radiation-induced segregation (RIS) in AL-6XN stainless steels has been investigated by transmission electron microscopy (TEM) with energy-dispersive X-ray spectroscopy. Specimens were irradiated with 100 keV H2+ ions from 1 dpa to 5 dpa at 380 °C to investigated the dose dependence of grain boundary RIS. A specimen was irradiated to 5 dpa at 290 °C to study the effect of irradiation temperature. The trends of Cr depletion and Ni enrichment with irradiation dose is similar to that of other austenitic steels reported in the literatures, but the higher concentration of hydrogen made the RIS profile wider. An abnormal phenomenon that the degree of RIS increased with decreasing irradiation temperature was found, indicating that with the retention of hydrogen in the steels, temperature dependence of RIS is dominated by the quantity of retained hydrogen, rather than by thermal segregation processes.