عنوان انگلیسی مقاله ISI
Studies on nanoporous glassy carbon as a new electrochemical capacitor material
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Studies on nanoporous glassy carbon as a new electrochemical capacitor material Studies on nanoporous glassy carbon as a new electrochemical capacitor material](/preview/png/9760233.png)
چکیده انگلیسی
A nanoporous glassy carbon (NPGC) used as a new electrochemical capacitor material has been developed and prepared from a novolac phenolic resin. This new porous carbon has a high specific capacity due to its large surface area and a high power density due to its nice bulk conductivity and nanoporous structure. In this paper, main factors that influence the pore structure and electrochemical performance of NPGCs were systematically investigated. The results showed that the porosity of carbonized resin increased with curing temperature up to 225 °C at which the resin can be cross-linked fully, facilitating activation agent molecules to diffuse inward. It was also found that high carbonization temperature helped crystallization of carbonized products, but the shrinkage of carbon skeleton made the extent of activation decrease. Meantime, increasing activation temperature may accelerate reaction rate and prolonging activation time may increase the extent of activation. However, too high activation temperature and too long activation time can make the carbon matrix cracked and distorted. Therefore, a maximum capacity of 203 F gâ1 and a conductivity of about 10 S cmâ1 was obtained for the NPGC sample prepared under suitable conditions, resulting in high power densities (6.5 kW kgâ1 carbon).
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Power Sources - Volume 148, 15 September 2005, Pages 121-128
Journal: Journal of Power Sources - Volume 148, 15 September 2005, Pages 121-128
نویسندگان
Yuehua Wen, Gaoping Cao, Yusheng Yang,