Failure analysis of a first stage IN738 gas turbine blade tip cracking in a thermal power plant
Keywords: قرارداد هدایت انتقال; First stage gas turbine blade; IN738LC nickel alloy; SEM; Corrosion pits; Coating degradation; TCP;