Synthesis and functionalization of SiO2 coated Fe3O4 nanoparticles with amine groups based on self-assembly
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
بیومتریال
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The purpose of this research was to synthesize amino modified Fe3O4/SiO2 nanoshells for biomedical applications. Magnetic iron-oxide nanoparticles (NPs) were prepared via co-precipitation. The NPs were then modified with a thin layer of amorphous silica. The particle surface was then terminated with amine groups. The results showed that smaller particles can be synthesized by decreasing the NaOH concentration, which in our case this corresponded to 35 nm using 0.9 M of NaOH at 750 rpm with a specific surface area of 41 m2 gâ 1 for uncoated Fe3O4 NPs and it increased to about 208 m2 gâ1 for 3-aminopropyltriethoxysilane (APTS) coated Fe3O4/SiO2 NPs. The total thickness and the structure of core-shell was measured and studied by transmission electron microscopy (TEM). For uncoated Fe3O4 NPs, the results showed an octahedral geometry with saturation magnetization range of (80-100) emu gâ1 and coercivity of (80-120) Oe for particles between (35-96) nm, respectively. The Fe3O4/SiO2 NPs with 50 nm as particle size, demonstrated a magnetization value of 30 emu gâ1. The stable magnetic fluid contained well-dispersed Fe3O4/SiO2/APTS nanoshells which indicated monodispersity and fast magnetic response.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: C - Volume 32, Issue 5, 1 July 2012, Pages 1043-1049
Journal: Materials Science and Engineering: C - Volume 32, Issue 5, 1 July 2012, Pages 1043-1049
نویسندگان
Mohammad E. Khosroshahi, Lida Ghazanfari,