Joining and microstructural development of Ni-Al-Ti sheets under ball collisions
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Ni-Al-Ti sheets were fabricated using a ball-collision technique at room temperature in an ambient atmosphere. The 0.5Â mm thick Ni, Al and Ti foils were stacked and fixed at the top of a vibration chamber and ball-treated for durations of between 5 and 30Â min. The microstructural evolution of the sheets was investigated as a function of the processing time and the mass of the ball. Joining of materials was considered to have occurred when materials at the interface plasticized, flowed and came into intimate contact under the high pressure developed by the ball collisions. The key parameters of the process were impact energy and processing time. Larger balls with higher impact energy were more effective for joining, and smaller balls were more effective for grain refinement. The transformation difference in grain refinement was attributed to the impact frequency, which appeared to be higher for the smaller balls. Ball collisions may have refined the grains of the Ni and Ti sheets to the nanometer scale, thereby destroying the initial rolling texture and inducing the formation of the fiber texture. The formation and stability of the ã1Â 1Â 1ã fiber texture in Ni were affected by the ball mass.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Acta Materialia - Volume 60, Issue 5, March 2012, Pages 2196-2208
Journal: Acta Materialia - Volume 60, Issue 5, March 2012, Pages 2196-2208
نویسندگان
S. Romankov, Y. Hayasaka, I.V. Shchetinin, J.M. Yoon,