• Two component polymer films leached to create film with voids on QCM.
• PMMA–PDLL mixed polymer films were formed by dip coating QCM.
• PDLL was leached from mixed film using a NaOH solution.
• Sensitivity for water vapor in nitrogen was increased.
• Only simple wet chemistry was used to make porous film.
We describe a novel and generally applicable approach for creating voids in films deposited on the surface of solid substrates. Such films are advantageous when a quartz crystal microbalance (QCM) is the basis of a sensor. We show that films with large void volumes produce more sensitive sensors than with the original film. Poly(methylmethacrylate) (PMMA) was used as the polymer layer deposited on a quartz crystal microbalance (QCM) to demonstrate our technique for the model system of water vapor analysis in flowing nitrogen gas. A film of pure PMMA on a QCM is a sensor for water vapor in a gas phase. A more sensitive sensor was created by dip coating QCM crystals into solutions containing mixtures of PMMA and poly(d,l-lactide) (PDLL) and then evaporating the solution films on the QCM crystals to form mixed polymer films of varying PDLL content. The PDLL was then removed from the mixed polymer films by exposure to a NaOH solution to form pure PMMA films having various void volumes. A leached PMMA film that originally contained 50% by weight PDLL had a 3.7 times larger QCM sensitivity for water vapor than a pure PMMA film.
Figure optionsDownload as PowerPoint slide
Journal: Analytica Chimica Acta - Volume 785, 27 June 2013, Pages 98–103