Different alkyl dimethacrylate mediated stearyl methacrylate monoliths for improving separation efficiency of typical alkylbenzenes and proteins

Monoliths were prepared in 530 μm I.D. fused silica capillaries via in situ copolymerization of stearyl methacrylate (SMA) with a dimethacrylate cross-linker in the presence of a binary porogenic solvent containing tert  .-butanol and 1,4-butanediol. Alkyl dimethacrylate cross-linkers other than the monomer were used to tune the monolith properties, and, as a result, an increase in the hydrophobicity of the final monoliths (the methylene selectivity αCH2αCH2 increased from 1.396 to 1.475) was observed through an increase in the molecular chain length between two methacrylate units from the 0.360 nm of ethylene glycol dimethacrylate to the 1.241 nm of 1.9-nonanediol dimethacrylate. Moreover, the hydrophobicity of the final monoliths was also greatly affected by the methyl group branch in the cross-linkers, among which the 2-methyl-1,8-octanediol dimethacrylate (2-Me-1,8-ODDMA) mediated monolith exhibited the highest hydrophobicity (αCH2αCH2 was 1.482) and fastest mass transfer kinetics (C-term was 9.14 ms). Besides the effective separation of six model proteins, the poly(SMA-co-2-Me-1,8-ODDMA) monolith also showed an improved performance in the separation of alkylbenzenes. The theoretical plate numbers reached 83 000 plates/m and 52 000 plates/m for thiourea (nonretained compound) and butylbenzene (retained compound), respectively, when using acetonitrile–water (70:30, v/v) as the mobile phase at a typical linear velocity of 1 mm/s. This improved performance towards small molecules was attributed to an increased mesopore proportion in the monolith and the faster dynamic process of mass transfer arising from novel tailoring of the monolith by choosing a suitable monomer/cross-linker pair.