Anode-supported thin electrolytes for operating at intermediate temperature have been successfully manufactured by tape casting and co-firing techniques that could be cost-effective for mass production of solid oxide fuel cell (SOFC) single cells. The characteristics of slurries and green tapes were investigated in order to optimize slurry compositions for thin-tape casting. When the amount of dispersant was 0.8 wt% and the weight ratio of the powder to binder solution was 2.5, the homogeneous microstructure of the green tape was obtained. The anode-supported electrolytes prepared by our process had the excellent microstructural characteristics such as gas permeability, porosity, and sintered microstructure at 1350 °C of the co-firing temperature and there were no defects. The power densities were evaluated according to the thickness of the anode-supported electrolyte, and a cell having 5μm thickness of the anode-supported electrolyte and anode active layer showed good electrochemical performance (0.55Wcm-2 at 700 °C) at intermediate temperatures.
Journal: International Journal of Hydrogen Energy - Volume 33, Issue 6, March 2008, Pages 1758–1768