Solvothermal synthesis, crystal structure, and second-order nonlinear optical properties of a new noncentrosymmetric gallium-organic framework material, [N(C3H7)4]3Ga3[C6H3(CO2)3]4

A novel noncentrosymmetric (NCS) gallium-organic framework material, [N(C3H7)4]3Ga3[C6H3(CO2)3]4 (CAUMOF-11) has been synthesized by a solvothermal reaction using Ga(NO3)3·xH2O, 1,3,5-C6H3(CO2H)3, N(C3H7)4Cl, HNO3, and HCON(CH3)2 at 180 °C. The structure of the reported material has been determined by single-crystal X-ray diffraction. CAUMOF-11 has an anionic three-dimensional framework with aligned four-coordinate GaO4 tetrahedra and 1,3,5-benzenetricarboxylate groups. Tetrapropylammonim cations reside within the channel and maintain the charge balance. Detailed structural analyses with full characterization including infrared spectroscopy, thermogravimetric analysis, elemental analysis, ion-exchange reactions, topotactic decomposition, and gas adsorption experiments are reported. Powder second-harmonic generating (SHG) measurements on CAUMOF-11, using 1064 nm radiation, exhibit SHG efficiency of 15 times that of α-SiO2 and the material is phase-matchable (type-1).

Graphical AbstractSecond-order nonlinear optical measurements on CAUMOF-11 reveal that the material is phase-matchable (type-1) with SHG efficiency of 15 times that of α-SiO2.Figure optionsDownload as PowerPoint slideHighlights
► A new NCS Ga-organic framework was solvothermally synthesized.
► CAUMOF-11 exhibits SHG efficiency of 15 times that of α-SiO2.
► Thermal decomposition of CAUMOF-11 crystal maintains the original morphology.