Ferroelectric perovskite-type barium copper niobate: BaCu1/3Nb2/3O3

A perovskite-type BaCu1/3Nb2/3O3 was prepared by high temperature reaction using BaCO3, CuO and Nb2O5. The X-ray powder diffraction pattern of this compound was indexed with the tetragonal cell with the lattice parameters of a=4.0464(4) and c=4.1807(4) Å (c/a=1.033). This compound had the tetragonal perovskite-type structure in which the B site was occupied statistically by Nb and Cu atoms. From high temperature X-ray powder diffraction patterns this compound had a phase transition from the tetragonal to cubic symmetry in the temperature range of 500–600 °C. The P–E and S–E hysteresis loops occurred at room temperature and the apparent maximum in the temperature dependence of the dielectric constant was observed at 520 °C. The temperature dependence of the inverse of magnetic susceptibility exhibited paramagnetic behavior.

High temperature X-ray powder diffraction of perovskite-type BaCu1/3Nb2/3O3.Figure optionsDownload as PowerPoint slide