Linear viscoelasticity of poly(acrylonitrile-co-itaconic acid)/1-butyl-3-methylimidazolium chloride extended from dilute to concentrated solutions

The solution rheology of poly(acrylonitrile-co-itaconic acid) (poly(AN-co-IA)) in 1-butyl-3-methylimidazolium chloride ([BMIM]Cl) spanning dilute, semidilute unentangled and entangled regimes were investigated. The exponents in the specific viscosity ηsp ∼ overlap parameter c[η] power law were 1, 2 and 4.7 for dilute, semidilute unentangled and entangled regimes, respectively, which were found to be consistent with the scaling prediction for neutral linear polymers in θ-solvent. For dilute solutions (lower than 0.9 wt.%), the linear viscoelastic responses were observed to be in good agreement with the Zimm model (Flory exponent ν = 0.5). While for semidilute unentangled solutions (between 0.9 and 8 wt.%), results obtained had been found to be consistent with Rouse model. Considering Flory exponent ν = 0.5 and the concentration dependences of the specific viscosity and relaxation time, it had been evaluated that poly(AN-co-IA) in [BMIM]Cl behaves as a neutral polymer in θ-solvent. It had also been suggested that according to the unusual deviation of Cox-Merz rule, poly(AN-co-IA)/[BMIM]Cl solutions are typical neutral polymeric liquids for the concentrated solutions but have shown a more complicated behavior at high deformation rates.

Figure optionsDownload as PowerPoint slide