Manipulating the surface properties of polyacrylamide with nitrogen plasma

Polyacrylamide (PAL) was physically adsorbed onto a hydroxylated silicon surface to form a uniform PAL film and the up–top PAL thin film was treated by nitrogen (N2) plasma for surface modification. The atomic composition of the modified surface of the PAL film adsorbed on silicon substrate was analyzed with Fourier Transform Infrared Spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The surface energy of PAL film was calculated from the data of contact angle of three-probe liquid. The FTIR results show an increase of peak intensity at 1214 cm−1 (NH2 stretch vibration) after the nitrogen plasma treatment, which confirms that the nitrogen was grafted to the PAL surface in the process of N2-plasma treatment. The XPS results show that the ratio of relative intensity of N1s to O1s increases with increasing the plasma treatment time, which further affirms the formation of the amine groups on the PAL surface after the nitrogen plasma treatment. The surface tension increases with increasing the plasma grafting time. However, the surface energy decreases rapidly at the early stage when stored in air and approaches to an equilibrium value. It suggests that some physically-adsorbed ions and alkyl radicals on PAL surface can rapidly lose their activities. The increase of the surface tension of the plasma treated PLA films is due to the amine groups covalently grafted to PAL surface.