Novel random poly(propylene isophthalate/adipate) copolyesters: Synthesis and characterization
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی آلی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Novel random poly(propylene isophthalate/adipate) copolyesters: Synthesis and characterization Novel random poly(propylene isophthalate/adipate) copolyesters: Synthesis and characterization](/preview/png/1400203.png)
چکیده انگلیسی
Poly(propylene adipate) (PPA) and poly(propylene isophthalate/adipate) (PPI-PPA) random copolymers of various compositions were synthesized in bulk and characterized in terms of chemical structure and molecular weight. Furthermore, the thermal behavior was examined by thermogravimetric analysis and differential scanning calorimetry. All the polymers showed a good thermal stability. At room temperature they appeared as semicrystalline materials, except the copolymers containing 20 and 30Â mol% of PI units: the main effect of copolymerization was a lowering in the amount of crystallinity and a decrease of melting temperature with respect to homopolymers. The crystalline phase of PPI and PPA was evidenced at high content of propylene isophthalate or propylene adipate units, respectively. Amorphous samples were obtained after melt quenching and an increment of Tg as the content of PI units is increased was observed. This behavior was explained as due to the stiff phenylene groups in the polymeric chain. The Wood equation was found to describe well Tg-composition data. Lastly, the presence of a rigid-amorphous phase was evidenced in the copolymers, differently from PPA homopolymer.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: European Polymer Journal - Volume 42, Issue 11, November 2006, Pages 2949-2958
Journal: European Polymer Journal - Volume 42, Issue 11, November 2006, Pages 2949-2958
نویسندگان
M. Soccio, L. Finelli, N. Lotti, M. Gazzano, A. Munari,