Well-dispersed nanocomposites of LDPE with spherical silica and laminar and fibrous silicates have been prepared by melt compounding with nanofiller compositions ranging from 50 to 5 wt%. Spatial dispersion and size domains of the aggregates in the composites series have been evaluated by electron microscopies (SEM and TEM). The methylene rocking (700–740 cm−1) and bending (1400–1480 cm−1) modes of LDPE in these composites were studied by FTIR spectroscopy. When the nanofiller is present in a 40 or 50 wt%, the amorphous phase of polyethylene adopts a monoclinic arrangement. This arrangement is due to the confinement induced by the nanofillers on the polymer matrix. When the fibrous silicate or the spherical silica are used as nanofillers, a dilution of the concentrated composite or annealing bring about a relaxing of the amorphous structure of the polymer, and the monoclinic-like conformations disappear. When the nanofiller is a laminar silicate, dilution or annealing only partly eliminate the monoclinic-like structure, which remains in all cases an important fraction of the polymeric matrix.
Journal: European Polymer Journal - Volume 45, Issue 1, January 2009, Pages 30–39