• Six series of alternative urethane-dimethacrylate monomers were tested.
• Monomers were tested to verify their potential use in dental restorative matrix.
• Six varied diisocyanates were used for the UDMA synthesis.
• Monomethacrylates containing form one to four oxyethylene units were used.
• HEMA/IPDI appeared to be the most promising alternative monomer.
ObjectiveThe aim was accomplished by a comparative analysis of the physicochemical properties of urethane-dimethacrylate (UDMA) monomers and their homopolymers with regard to the properties of basic dimethacrylates used presently in dentistry. The homologous series of UDMA were obtained from four oligoethylene glycols monomethacrylates (HEMA, DEGMMA, TEGMMA and TTEGMMA) and six diisocyanates (HMDI, TMDI, IPDI, CHMDI, TDI and MDI).MethodsPhotopolymerization was light-initiated with the camphorquinone/tertiary amine system. Monomers were tested for viscosity and density. Flexural strength, flexural modulus, hardness, water sorption and polymerization shrinkage of the polymers were studied. The glass transition temperature and the degree of conversion were also discussed.ResultsHEMA/IPDI appeared to be the most promising alternative monomer. The monomer exhibited a lower viscosity and achieved higher degree of conversion, the polymer had lower water sorption as well as higher modulus, glass temperature and hardness than Bis-GMA. The polymer of DEGMMA/CHMDI exhibited lower polymerization shrinkage, lower water sorption and higher hardness, however it exhibited lower modulus when compared to HEMA/TMDI. The remaining monomers obtained from HEMA were solids. Monomers with longer TEGMMA and TTEGMMA units polymerized to rubbery networks with high water sorption. The viscosity of all studied UDMA monomers was too high to be used as reactive diluents.SignificanceThe systematic, comparative analysis of the homologous UDMA monomers and corresponding homopolymers along with their physico-mechanical properties are essential for optimizing the design process of new components desirable in dental formulations. Some of the studied UDMA monomers may be simple and effective alternative dimethacrylate comonomers.
Journal: Dental Materials - Volume 30, Issue 12, December 2014, Pages 1336–1344