Effect of surface pre-treatments on the zirconia ceramic–resin cement microtensile bond strength
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد بیومتریال
پیش نمایش صفحه اول مقاله
Effect of surface pre-treatments on the zirconia ceramic–resin cement microtensile bond strength
چکیده انگلیسی

ObjectiveTo evaluate the influence of different surface treatments on the microtensile bond strength of resin cement to zirconia ceramic.Materials and methodsTwelve cylinder-shaped (∅ 12 × 5.25 mm high) blocks of a commercial zirconium-oxide ceramic (Cercon® Zirconia, DENTSPLY) were randomly divided into 4 groups (n = 3), based on the surface treatment to be performed: (1) airborne particle abrasion with 125 μm Al2O3 particles (S); (2) selective infiltration etching (SIE); (3) experimental hot etching solution applied for 30 min (ST) and (4) no treatment (C). Paradigm MZ100 blocks (3M ESPE) were cut into twelve cylinders of 4 mm in thickness. Composite cylinders were bonded to conditioned ceramics using a resin cement (Calibra®, DENTSPLY), in combination with the proprietary adhesive system. After 24 h bonded specimens were cut into microtensile sticks and loaded in tension until failure. Bond strength data were analyzed with Kruskall–Wallis and Dunn's Multiple Range test for multiple comparisons (p < 0.05). Failure mode distribution was recorded and the interfacial morphology of debonded specimens was analyzed using a scanning electron microscope (SEM).ResultsBond strength values achieved after SIE and ST treatment were significantly higher than after S treatment and without any treatment (p < 0.05). Premature failures were mostly recorded in the S group.SignificanceConditioning the high-strength ceramic surface with SIE and ST treatments yielded higher bond strengths of the resin cement than when zirconia ceramic was treated with airborne particle abrasion or left untreated.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Dental Materials - Volume 27, Issue 10, October 2011, Pages 1024–1030
نویسندگان
, , , , , , ,