Polymerization shrinkage kinetics of dimethacrylate resin-cements

ObjectivesTo determine polymerization shrinkage-strain (SY) and shrinkage-stress (SZ) of six resin-cements and to compare their performance with the aid of degree of conversion (DC) data.MethodsVariolink 2 (VL2), Multilink Automix (MA), Multilink Sprint (MS, all Ivoclar-Vivadent), Nexus 2 (NX2), Maxcem (MX, both Kerr) and RelyX Unicem (RX, 3M-Espe) were investigated. MS, MX and RX were self-adhesive; others require a bonding-agent. All measurements were conducted at 23 °C for 60 min (n = 5), except 80 min for RX, with materials self-cured only (sc) and dual-cured (dc); NX2 and VL2 were additionally light-cured only (lc). SY was measured by the bonded-disk method [Watts DC, Cash AJ. Determination of polymerization shrinkage kinetics in visible-light-cured materials: methods development. Dent Mater 1991;7(4):281–7; Watts DC, Marouf AS. Optimal specimen geometry in bonded-disk shrinkage-strain measurements on light-cured biomaterials. Dent Mater 2000;16(6):447–51]; SZ by the Bioman instrument [Watts DC, Satterthwaite JD. Axial shrinkage-stress depends upon both C-factor and composite mass. Dent Mater 2008;24(1):1–8 [Epub October 24, 2007]; Watts DC, Marouf AS, Al-Hindi AM. Photo-polymerization shrinkage-stress kinetics in resin-composites: methods development. Dent Mater 2003;19(1):1–11]. Light-cure was achieved by QTH at 500 mW/cm2. The respective DCs were measured under the same conditions by FTIR–ATR spectroscopy. Data were analyzed by One-Way ANOVA plus Bonferroni test, and by t-test, at p < 0.05.ResultsDC by self-curing was less than the DC by dual-curing, for all cements. Shrinkage-strain ranged from 1.77 to 5.29% and shrinkage-stress from 3.36 to 10.37 MPa. NX2 and VL2 were not significantly different, when light-cured only. Except for RX, sc and dc shrinkage-strain varied maximally by 0.4%. MX showed the highest SY, RX the lowest. When sc, RX initially expanded by <0.5% (t ∼ 5 min). For most materials, SY correlated with their filler loading. The highest stress with sc was exerted by MX, and when dc by MS, which was not statistically different from MX.SignificanceShrinkage data of resin-cements are of intrinsic clinical importance. Self-cure, despite a lower DC, did not necessarily result in a lower SY compared to dual-cure. SY-rate and SZ development depend upon cure mode and SY upon filler fraction.