Cross-link density evaluation through softening tests: Effect of ethanol concentration
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد بیومتریال
پیش نمایش صفحه اول مقاله
Cross-link density evaluation through softening tests: Effect of ethanol concentration
چکیده انگلیسی

ObjectivesThe aim of this study was to investigate whether the ethanol concentration used would influence the outcomes obtained through softening tests when comparing light-activation modes.MethodsDisc specimens (n = 20) of Filtek Z250 and Filtek Z100 (3M ESPE) were light activated by standard (S) and pulse-delay (PD) modes. Initial Knoop hardness (KHN) measurements were performed 24 h after dry storage at 37 °C. Half of the specimens (n = 10) of each resin-composite were stored in absolute ethanol (100%) and the other half in 75% ethanol solution, for 24 h at room temperature, and KHN was determined anew. Initial hardness data were submitted to Student's t-test (p = 0.05). Percentages of hardness decrease were analyzed by two-way ANOVA followed by pairwise Tukey's test (p = 0.05). The statistical analyses were performed separately for each resin-composite.ResultsNo statistically significant differences were observed between standard and pulse-delay modes for initial Knoop hardness values. After storage in 75% ethanol solution, KHN was decreased in all cases but no significant differences were detected between light-activation modes (Filtek Z250: PD = 12.6%, S = 13.5%; Filtek Z100: PD = 13.5%, S = 11.8%) regardless of the resin-composite tested. After absolute ethanol storage, higher decrease in KHN were observed. Samples light-activated by the PD mode (Filtek Z250 = 20.4% and Filtek Z100 = 16.9%) exhibited significantly higher percentage decrease of KHN than specimens light-activated by the standard mode (Filtek Z250 = 14.1% and Filtek Z100 = 8.8%), regardless of the resin-composite tested.ConclusionThe ethanol concentration affected the outcomes of the softening test.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Dental Materials - Volume 24, Issue 2, February 2008, Pages 199–203
نویسندگان
, , , , , ,