Tensile bond strength of Er,Cr:YSGG laser-irradiated human dentin and analysis of dentin–resin interface

ObjectivesAs the bond strength of composite resin to Er,Cr:YSGG laser-irradiated dentin has not yet been evaluated, the objectives of this study were to investigate the tensile bond strength and to analyze the resin–dentin interface among bur-cut/acid-etched, Er,Cr:YSGG laser-ablated/acid-etched and Er,Cr:YSGG laser-ablated human dentin.MethodsCrown dentin disks prepared from extracted human third permanent molars were used for the observation of surface morphological changes by scanning electron microscope (SEM). The laser energy parameters were 3.5 W and 20 Hz with water spray (air pressure level, 80%; water pressure level, maximum level). Another group of crown dentin disks were prepared for composite resin restoration and observation of resin–dentin bond interface after demineralization in 6N hydrochloric acid (HCl) for 1 min and deproteinization in 1% sodium hypochlorite solution (NaOCl) for 10 min. The tensile bond strengths of the three groups were measured by a universal testing machine at a crosshead speed of 0.5 mm/min. Fracture types at the dentin–resin interface were analyzed using the digital stereoscopic microscope and fractured surfaces of the debonded specimens were examined by SEM.ResultsAll three groups showed that the treated surfaces were free of dentin debris and smear layer. The peritubular dentin protruded from the surrounding intertubular dentin after laser irradiation. The dentin–resin interface treated with Er,Cr:YSGG laser irradiation and acid etching demonstrated numerous resin tags converging into a bulge and then diverging again. The length of resin tags was greater than 100 μm. The tensile bond strengths of bur-cut/acid-etched, aser-ablated/acid-etched and laser-ablated human dentin were 5.37 ± 1.51, 5.17 ± 1.41 and 3.29 ± 0.86 MPa, respectively. No statistical significance was found between the bur-cut/acid-etched and laser-ablated/acid-etched groups. The predominant fracture modes of bur-cut/acid-etched, laser-ablated/acid-etched and laser-ablated human dentin were Type 1 (50%), Type 2 (70%) and Type 1 (70%), respectively.SignificanceEr,Cr:YSGG laser irradiation affects adversely adhesion of resin to dentin but acid etching following laser irradiation could increase the tensile bond strength as high as that of bur-cut/acid-etched human dentin.